Asbestos Free Jointing Sheet

There are various Asbestos Free Jointing Sheet offered by us that are suitable for being used in Automotive, Power, Refineries, Food, Petro-chemical, Sugarcane and Railways among others. It is specifically designed to satisfy the growing demand for numerous aggressive chemicals used by industry today. It can also be used for sealing oils, fuels, gases, freons, and general application in paper & pulp industry for application in pipelines, radiators, boilers and many other instances of flanged joints. The sheet is manufactured in various types as per the need and requirement of the various industries. They are very efficient and resistant to a variety of chemicals. The Asbestos Free Jointing Sheet are easy to mold. They are highly effective and made for long term use.

BETAFLEX T-200 ASBESTOS FREE GASKET JOINTING SHEET

General data:
  • Material Composition : Gasket material based on Mineral Fibre & Organic Fibre & Elastomers
  • (Type of fibres) Binders :NBR
Operating Condition
  • Max.Peak Temp : 200 Degree C
  • Max. Continuous Temp Max. : 150 Degree C
  • Operating Pressure : 40 Kg/cm

Specification

Proer- Ties

Test Method


Unit

Specified Value


Density



Gm/ cm3


1.70 - 1.90

Tensile Strength





Acc To Astm F152(Across
Grain)



N/mm


> 7


Acc To Din52910 (ACROSS Grain


N/mm



Compressibility

ASTM F36A


%

7-15

Recovery

ASTM F36A


%

> 40


Fluid Absorption


ASTM F 146




In Astm Oil No. 3




Increase In Mass



%

> 20


Increase In Thickness



%

> 15


In Fuel B

ASTM F 146




Increase In Mass



%

> 20

Increase In Thickness



%

> 20

In Water/Antifreeze


ASTM F 146




Increase In Mass




%

< 15


Increase In Thickness



< 10

Increase In Mass

Ignition Loss


DIN 52911


%


< 40

Sealability Against Nitrogen


DIN 3535


cm3 / min.



Stress Resistance



Technical Details 

BETAFLEX T-250 ASBESTOS FREE GASKET JOINTING SHEET

  • Material Composition(Type of fibres) : Gasket material Based on Aramid fiber, Organic Fibre.& Mineral Fibre.
  • Binders :NBR

Operating Condition

  • Max. Peak Temp : 250 Degree C
  • Max. Continuous : 180 Degree C
  • Max. Operating Pressure
  • Physical Properties: 70Kg/cm

Specification

Properties

Test
Method

Unit

Specified Value

Density

 

gm/cm

1.70-2.00

Tensile Strength

 

 

 

(A)ACC To ASTMF 152 (ACROSS GRAIN)

 

N/mm

>7

(B )ACC To DIN 52910 (ACROSS GRAIN)

 

 N/mm

>5

Compressibility

ASTMF36A

%

5-15

Recovery

ASTMF36A

%

>40

Flu I D Absorption

ASTMF146

 

 

(A)INASTMOILNO.3

 

 

 

Increase In Mass

 

%

< 1 5

Increase In Thickness

 

%

< 1 0

(B ) I N FUELB

ASTMF146

 

 

Increase In Mass

 

%

< 1 0

Increase In Thickness

 

%

< 1 0

(C) I N WATER/ANTIFREEZE

ASTMF146


 

Increase In Mass

 

%

< 1 5

Increase In Thickness

 

%

<7

Ignition Loss

DIN52911

%

<40

S Ealab I L Ity Against Nitrogen

DIN3535

cm /min.


Standard Sheet Size

 

1500x2000mm,1500x1500mm 1500x4500mm,1500x3000mm,

Thickness

 

0.40mmto 6.00mm(For Non-Metallic Range) 0.80mmto6.00mm(For Metallic Range)

Tolerance

Thickness

<1mm=+/-0.10mm >1mm=+/-10%

Length

+/-50mm

Width

+/-50mm

Technical Details 

BETAFLEX T-330 ASBESTOS FREE GASKET JOINTING SHEET

General data:
  • Material Composition (Type of fibres) : Aramid Fibre, Mineral Fiber
  • Binders : NBR
Operating Condition
  • Max. Peak Temp : 330 Degree C
  • Max. Continuous Temp Max. : 240 Degree C
  • Operating Pressure : 100 Kg/cm

Specification

Properties

Test
Method

Unit

Specified Value

Density

 

gm/cm

1.70-2.00

Tensile Strength

 

 

 

(A)ACC To ASTMF 152 (ACROSS GRAIN)

 

N/mm

>8

(B )ACC To DIN 52910 (ACROSS GRAIN)

 

N/mm

>5

Compressibility

ASTMF36A

%

7-15

Recovery

ASTMF36A

%

>50

Flu I D Absorption

ASTMF146

 

 

(A)INASTMOILNO.3

 

 

 

Increase In Mass

 

%

< 15

Increase In Thickness

 

%

< 10

(B ) I N FUELB

ASTMF146

 

 

Increase In Mass

 

%

< 10

Increase In Thickness

 

%

< 10

(C) I N WATER/ANTIFREEZE

ASTMF146

 

 

Increase In Mass

 

%

< 15

Increase In Thickness

 

%

<7

Ignition Loss

DIN52911

%

<35

Sealability Against Nitrogen

DIN3535

cm /min.

< 1.0

 

Technical Details 

BETAFLEX T-450 CF ASBESTOS FREE GASKET JOINTING SHEET

General Data

 

  • Material Composition(Type of fibres) : Gasket material based on Aramid Fiber, Carbon Fiber
  • Binders : NBR

 

Operating Condition
  • Max.Peak Temp : 450 Degree C
  • Max. Continuous Temp :350 Degree C
  • Max. Operating Pressure : 150 Kg/cm2

Specification

Properties

TEST
METHOD

UNIT

SPECIFIED
VALUE

Density

 

gm/cm3

1.70 - 2.00

Tensile Strength

 

 

 

(A) ACC To ASTM F152(ACROSS GRAIN)

 

N/mm2

> 8

(B) ACC To DIN52910 (ACROSS GRAIN)

 

N/mm2

>6

Compressibility

ASTM F36A

%

5 - 15

Recovery

ASTM F36A

%

> 50

Fluid Absorption

ASTM F 146

 

 

(A) IN ASTM OIL NO. 3

 

 

 

Increase In Mass

 

%

< 1 0

Increase In Thickness

 

%

< 8

(B ) IN FUEL B

ASTM F 146

 

 

Increase In Mass

 

%

< 10

Increase In Thickness

 

%

<7

(C) IN WATER/ANTIFREEZE

ASTM F 146

 

 

Increase In Mass

 

%

< 10

Increase In Thickness

 

%

< 7

Ignition Loss

DIN 52911

%

< 30

Sealability Against Nitrogen

DIN 3535

cm /min3

< 0.5

STRESS RESISTANCE

 

 

 

16h 300 Degree C

DIN 52913

N/mm3

20

16h 175 Degree C

DIN 52913

N/mm3

30


Technical Details 

BETAFLEX T-450 GF ASBESTOS FREE GASKET JOINTING SHEET

General Data

 

  • Composition(Type of fibres) : Gasket material based on Aramid Fibre, Glass fibre Fibre, Mineral fibre, inorganic fillers .
  • Binders : NBR

 

Operating Condition
  • Max.Peak Temp : 450 Degree C
  • Max. Continuous Temp : 350 Degree C
  • Max. Operating Pressure :150 Kg/cm

Specification

Properties

TEST METHOD

UNIT

SPECIFIED VALUE

Density

 

gm/cm3

1.70 - 2.00

Tensile Strength

 

 

 

(A) ACC To ASTM F152(ACROSS GRAIN)

 

N/mm2

> 8

(B) ACC To DIN52910 (ACROSS GRAIN)

 

N/mm2

>6

Compressibility

ASTM F36A

%

7 - 15

Recovery

ASTM F36A

%

> 50

Fluid Absorption

ASTM F 146

 

 

(A) IN ASTM OIL NO. 3

 

 

 

Increase In Mass

 

%

< 1 0

Increase In Thickness

 

%

< 8

(B ) IN FUEL B

ASTM F 146

 

 

Increase In Mass

 

%

< 1 0

Increase In Thickness

 

%

<7

(C) IN WATER/ANTIFREEZE

ASTM F 146

 

 

Increase In Mass

 

%

< 1 0

Increase In Thickness

 

%

< 7

Ignition Loss

DIN 52911

%

< 30

Sealability Against Nitrogen

DIN 3535

cm /min.3

< 1 0

STRESS RESISTANCE

 

 

 

16h 300 Degree C

DIN 52913

N/mm3

25

16h 175 Degree C

DIN 52913

N/mm3

30

 

Technical Details 

Asbestos Free Gasket Jointing Sheet Betaflex T- 405

Applications: This product Suitable for high performance, oil resistant gasket material with excellent thermal, chemical & mechanical properties. suitable for fuel, alcohols, gases hydrocarbons, steam, water, cooling liquid, most diluted acid alkalies for high stress conditions.

General data:

  • Material Composition (Type of fibres): Gasket material Based on Aramid fiber, Inorganic Fibre.& Mineral Fibre.
  • Binders: NBR

OPERATING CONDITION

  • Max.Peak Temp: 405 deg C

  • Max. Continuous Temp Max.: 250 deg C

  • Max. Operating Pressure:100 Kg/cm.

Physical Properties: The following Information applies to material thickness 2.00 mm.

PROER- TIES

TEST METHOD

UNIT

SPECIFIED VALUE

DENSITY


gm/cm 3

1.70- 2.00

TENSILE STRENGTH




(a)ACC to ASTM F152 (ACROSS GRAIN)


N/mm 2

>10

(b) ACC to DIN52910 (ACROSS GRAIN)


N/mm 2

>7

COMPRESSIBILITY

ASTM F36A

%

6-12

RECOVERY

ASTM F36A

%

>50

FLUID ABSORPTION

ASTM F 146



(a) IN ASTM OIL NO. 3




INCREASE IN MASS


%

<10

INCREASE IN THICKNESS


%

<10

(b) IN FUEL B

ASTM F 146



INCREASE IN MASS


%

<10

INCREASE IN THICKNESS


%

<10

(c) IN WATER/ ANTIFREEZE

ASTM F 146



INCREASE IN MASS


%

<15

INCREASE IN THICKNESS


%

<7

IGNITION LOSS

DIN 52911

%

<35

SEALABILITY AGAINST Nitrogen

DIN 3535

cm/min.3

< 1.0

STRESS RESISTANCE




16h300 deg C

DIN 52913

N/mm 2

18

6h175 deg C

DIN 52913

N/mm 2




Technical Details 

Asbestos Free Gasket Jointing Sheet Betaflex T- 405-High Stress (Hs)

Applications: This product Suitable for high performance, oil resistant gasket material with excellent thermal, chemical & mechanical properties. suitable for fuel, alcohols, gases hydrocarbons, steam, water, cooling liquid, most diluted acid alkalies for high stress conditions.

General data:

Material Composition (Type of fibres): Mineral Fibre, Synthetic

Binders: Fibre Aramid Fibre, High quality NBR

OPERATING CONDITION

  • Max.Peak Temp: 405 deg C
  • Max. Continuous Temp Max.: 320 deg C
  • Continuous Temp. with steam: 250 deg C
  • Max. Operating Pressure:150 Kg/cm.

Physical Properties: The following Information applies to material thickness 2.00 mm.

PROER- TIES

TEST METHOD

UNIT

SPECIFIED VALUE

DENSITY


3

1.70- 2.00

TENSILE STRENGTH




(a)ACC to ASTM F152 (ACROSS GRAIN)


2

>14

(b) ACC to DIN52910 (ACROSS GRAIN)


2

>11

COMPRESSIBILITY

ASTM F36A

%

6-12

RECOVERY

ASTM F36A

%

>50

FLUID ABSORPTION

ASTM F 146



(a) IN ASTM OIL NO. 3




INCREASE IN MASS


%

<10

INCREASE IN THICKNESS


%

<8

(b) IN FUEL B

ASTM F 146



INCREASE IN MASS


%

<10

INCREASE IN THICKNESS


%

<7

(c) IN WATER/ ANTIFREEZE

ASTM F 146



INCREASE IN MASS


%

<15

INCREASE IN THICKNESS


%

<7

IGNITION LOSS

DIN 52911

%

<30

SEALABILITY AGAINST Nitrogen

DIN 3535

3

< 0.5

STRESS RESISTANCE




deg

DIN 52913

2

20

deg

DIN 52913

2

30

Technical Details 